Título: Avaliação experimental da interação de paredes de blocos de concreto de alta resistência sob ações verticais
Experimental evaluation of the interaction of high strenght concrete block walls under vertical loads
Autor(es): Castro, Lucas de Oliveira
Abstract: Este trabalho tem como objetivo avaliar a interação entre paredes de alvenaria estrutural de blocos de concreto de alto desempenho (CAD), sob ações verticais. Foram ensaiadas duas séries de painéis em formato H em escala real, com amarração direta, sendo três painéis com a parede central (alma) apoiada e três painéis sem o apoio. O programa experimental abrangeu também ensaios de caracterização física e mecânica dos blocos, dos prismas de dois blocos e da argamassa. Foram obtidos os módulos de deformação, tanto para as argamassas, blocos e prismas, quanto para os painéis de alvenaria e o coeficiente de Poisson para os blocos. Para escolha do traço de argamassa, foram avaliadas três séries de prismas, utilizando-se argamassas com resistências médias à compressão iguais a 40% (série 1), 70% (série 2) e 100% (série 3) da resistência característica à compressão dos blocos, respectivamente, referida à área bruta. Todas as argamassas utilizadas no programa experimental foram dosadas utilizando o método proposto por Santos (2014). Com base nos resultados dessas séries, foram confeccionadas e ensaiadas duas novas séries, ambas utilizando a argamassa da série 2, sendo uma com argamassamento parcial nas paredes longitudinais (série 4) e outra com argamassamento total para sua caracterização (série 5). Os painéis de alvenaria utilizaram o segundo traço em sua confecção. Os resultados dos prismas permitiram avaliação da eficiência prisma/bloco, além dos modos de ruptura, que variaram para as diferentes configurações de ensaio. Os valores do módulo de deformação e coeficiente de Poisson médio mostraram uma boa relação com as recomendações da norma. A análise de variância das amostras submetidas à compressão (prismas) mostra que existe influência da resistência da argamassa na resistência à compressão dos prismas. Os resultados dos ensaios de painéis mostraram que os modos de ruptura foram predominantemente na parede central, abaixo do ponto de aplicação da carga com trincas na diagonal e escalonada e que existe transferência de carga da parede central (alma) para as abas, principalmente no trecho inferior dos painéis.
This study aims to evaluate the interaction between structural masonry walls of high strenght concrete blocks, under vertical loads. Two panels series were studied in format “H”, full scale and direct bond, three panels with the central wall (web) support and three panels without central wall support. The experimental program also included tests of physical and mechanical characterizations of mortar, blocks and prisms of two blocks. The modulus of elasticity were obtained for mortars, blocks, prism and for masonry painels; Poisson’s ratio was obtained for blocks. Three prisms series were evaluated to select the mortar’s line, each using a different mortar trace with mean resistance to compression equal to 40% (series 1), 70% (series 2) and 100% (series 3) of the block’s compressive strength characteristic, referred to its gross area. All mortars used in the experimental program were dosaged using the method proposed by Santos (2014). Two new series (serie 4 and serie 5) were made based on the results of these three series, both using the mortar from serie 2; serie 4 was made with partial mortar on longitudinal walls, while serie 5 was made with full mortar for its characterization. The results of the prisms allowed the evaluation of the prism/block efficiency, in addition to the failure modes, which changed for different test configurations. The values of the modulus of elasticity and Poisson’s ratio average showed good relationship with standard recommendations. The variance analysis of the samples subjected to compression (prism) shows that there is influence of mortar strength in the compression resistance of the prisms. To making masonry panels was used the second mortar trace. The results of the panel test show that the failure mode was predominantly in the central wall, below the load application point, with diagonal and staggered cracks, and that there is charge transfer (web) for the flages, mainly in the bottom section of the panels.
Palavras-chave: Engenharia de estruturas
Alvenaria
Blocos de concreto
CNPq: Engenharia Civil
Editor: Universidade Federal de Viçosa
Titulação: Mestre em Engenharia Civil
Citação: CASTRO, Lucas de Oliveira. Avaliação experimental da interação de paredes de blocos de concreto de alta resistência sob ações verticais. 2015. 163f. Dissertação (Mestrado em Engenharia Civil) - Universidade Federal de Viçosa, Viçosa. 2015.
Tipo de Acesso: Acesso Aberto
URI: http://www.locus.ufv.br/handle/123456789/6522
Data do documento: 21-Ago-2015
Aparece nas coleções:Engenharia Civil

Arquivos associados a este item:
Arquivo Descrição TamanhoFormato 
texto completo.pdftexto completo5,72 MBAdobe PDFThumbnail
Visualizar/Abrir


Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.