Avaliação do desempenho quanto à estanqueidade de juntas sujeitas a envelhecimento acelerado, utilizadas em sistemas de vedação vertical externa em alvenaria para estruturas de aço

Show simple item record

dc.contributor Paes, José Luiz Rangel
dc.contributor Veríssimo, Gustavo de Souza
dc.contributor.advisor Pedroti, Leonardo Gonçalves
dc.creator Franco, Rayane Neves
dc.date.accessioned 2019-05-08T13:49:36Z
dc.date.available 2019-05-08T13:49:36Z
dc.date.issued 2019-02-07
dc.identifier.citation FRANCO, Rayane Neves. Avaliação do desempenho quanto à estanqueidade de juntas sujeitas a envelhecimento acelerado, utilizadas em sistemas de vedação vertical externa em alvenaria para estruturas de aço. 2019. 153 f. Dissertação (Mestrado em Engenharia Civil) - Universidade Federal de Viçosa, Viçosa. 2019. pt-BR
dc.identifier.uri http://www.locus.ufv.br/handle/123456789/25076
dc.description.abstract No âmbito das construções em aço, tem sido comum a ocorrência de problemas de estanqueidade nas juntas e interfaces entre alvenaria e estrutura de aço, o que leva a uma deterioração precoce da estrutura e diminui a vida útil da edificação. Neste trabalho aborda-se a avaliação do desempenho quanto à estanqueidade de juntas típicas utilizadas em sistemas de vedação vertical externa (SVVE) em alvenaria para estruturas de aço, sujeitas a envelhecimento acelerado. Para isso, foi desenvolvido um painel radiante seguindo as prescrições da ABNT NBR 15575-4:2013 e foram construídos dois exemplares de um modelo experimental com junta vertical. As juntas do modelo foram inicialmente tratadas com selante à base de poliuretano, e posteriormente com manta de elastômero EPDM. Foram realizados ensaios de exposição à ação do calor e choque térmico e ensaios de estanqueidade à água, com base na norma citada. No caso das juntas tratadas com manta de elastômero EPDM, também foram realizados ensaios de estanqueidade com a face externa do modelo pintada com tinta acrílica. Observou-se que após os ensaios de exposição à ação do calor e choque térmico o selante à base de poliuretano e a manta de elastômero EPDM não sofreram degradações perceptíveis e que houve o surgimento de fissuras horizontais na face interna dos exemplares do modelo experimental. As manchas de umidade, identificadas no modelo experimental nos ensaios de estanqueidade à água, se deram pela passagem de água por meio das fissuras horizontais introduzidas no ensaio de exposição à ação do calor e choque térmico e não pela junta vertical para ambos os tratamentos. Existem fortes evidências de que a fissuração horizontal pode ter sido induzida pela presença dos grampos inseridos nas juntas horizontais, que acabaram transferindo o deslocamento devido à dilatação do pilar de aço para a alvenaria. A inexistência de manchas de umidade nos exemplares com face externa pintada com tinta acrílica, após o ensaio de estanqueidade à água, evidencia que a tinta acrílica foi capaz de selar as fissuras na superfície da argamassa e confirma que o tratamento da junta vertical com manta de elastômero EPDM apresentou bom desempenho quanto à estanqueidade à água. pt-BR
dc.description.abstract In the context of steel constructions, it has been common the occurrence of watertightness problems in the joints and interfaces between masonry and steel structure, which leads to an early deterioration of the structure and decreases the service life of the building. This research aims to evaluate the performance in terms of watertightness of typical joints used in external vertical sealing systems (EVS) in masonry for steel structures, subjected to accelerated aging. For this purpose, a radiant panel was developed following the requirements of ABNT NBR 15575-4:2013 and two specimens of an experimental model with vertical joint were constructed. The joints of the experimental model were treated with a polyurethane sealant, and later treated with an EPDM rubber splice tape. It was carried out heat exposure and thermal shock tests and watertightness tests, based on the cited standard. In the case of joints treated with EPDM rubber splice tape, the watertightness tests were also carried out with the external face of the experimental model painted with acrylic paint. It was noted that after the heat exposure and thermal shock tests, the polyurethane sealant and the EPDM rubber splice tape did not suffer noticeable degradation and it was also noted that horizontal cracks appeared on the inner face of the specimens of the experimental model. The moisture spots identified on the experimental model during the water tightness tests occurred due to the passage of water through the horizontal cracks introduced in the heat exposure and thermal shock test and not by the vertical joint for both treatments. There are strong evidences that horizontal cracking may have been induced by the presence of the connectors inside the horizontal joints, which eventually transferred the displacement suffered by the steel pillar due to the expansion to the masonry. The absence of moisture spots on the experimental model with its external face painted with acrylic paint, after the watertightness test, shows that the acrylic paint was able to stagnate the cracks in the surface of the mortar and confirms that the treatment of the vertical joint with EPDM rubber splice tape showed good performance in terms of watertightness. en
dc.language.iso por pt-BR
dc.publisher Universidade Federal de Viçosa pt-BR
dc.rights Acesso Aberto pt-BR
dc.subject Aço - Estruturas pt-BR
dc.subject Vedação (Tecnologia) pt-BR
dc.subject Alvenaria pt-BR
dc.subject Juntas (Engenharia) pt-BR
dc.subject Desempenho pt-BR
dc.title Avaliação do desempenho quanto à estanqueidade de juntas sujeitas a envelhecimento acelerado, utilizadas em sistemas de vedação vertical externa em alvenaria para estruturas de aço pt-BR
dc.title Evaluation of the performance in terms of watertightness of joints used in external vertical sealing systems in masonry for steel structures, subjected to accelerated aging en
dc.type Dissertação pt-BR
dc.subject.cnpq Processos construtivos pt-BR
dc.creator.lattes http://lattes.cnpq.br/2461801800129295 pt-BR
dc.degree.grantor Universidade Federal de Viçosa pt-BR
dc.degree.department Departamento de Engenharia Civil pt-BR
dc.degree.program Mestre em Engenharia Civil pt-BR
dc.degree.local Viçosa - MG pt-BR
dc.degree.date 2019-02-07
dc.degree.level Mestrado pt-BR


Files in this item

This item appears in the following Collection(s)

  • Engenharia Civil [384]
    Teses e dissertações defendidas no Programa de Pós-Graduação em Engenharia Civil

Show simple item record

Search DSpace


Browse

My Account