Título: Avaliação do desempenho quanto à estanqueidade de juntas sujeitas a envelhecimento acelerado, utilizadas em sistemas de vedação vertical externa em alvenaria para estruturas de aço
Evaluation of the performance in terms of watertightness of joints used in external vertical sealing systems in masonry for steel structures, subjected to accelerated aging
Autor(es): Franco, Rayane Neves
Abstract: No âmbito das construções em aço, tem sido comum a ocorrência de problemas de estanqueidade nas juntas e interfaces entre alvenaria e estrutura de aço, o que leva a uma deterioração precoce da estrutura e diminui a vida útil da edificação. Neste trabalho aborda-se a avaliação do desempenho quanto à estanqueidade de juntas típicas utilizadas em sistemas de vedação vertical externa (SVVE) em alvenaria para estruturas de aço, sujeitas a envelhecimento acelerado. Para isso, foi desenvolvido um painel radiante seguindo as prescrições da ABNT NBR 15575-4:2013 e foram construídos dois exemplares de um modelo experimental com junta vertical. As juntas do modelo foram inicialmente tratadas com selante à base de poliuretano, e posteriormente com manta de elastômero EPDM. Foram realizados ensaios de exposição à ação do calor e choque térmico e ensaios de estanqueidade à água, com base na norma citada. No caso das juntas tratadas com manta de elastômero EPDM, também foram realizados ensaios de estanqueidade com a face externa do modelo pintada com tinta acrílica. Observou-se que após os ensaios de exposição à ação do calor e choque térmico o selante à base de poliuretano e a manta de elastômero EPDM não sofreram degradações perceptíveis e que houve o surgimento de fissuras horizontais na face interna dos exemplares do modelo experimental. As manchas de umidade, identificadas no modelo experimental nos ensaios de estanqueidade à água, se deram pela passagem de água por meio das fissuras horizontais introduzidas no ensaio de exposição à ação do calor e choque térmico e não pela junta vertical para ambos os tratamentos. Existem fortes evidências de que a fissuração horizontal pode ter sido induzida pela presença dos grampos inseridos nas juntas horizontais, que acabaram transferindo o deslocamento devido à dilatação do pilar de aço para a alvenaria. A inexistência de manchas de umidade nos exemplares com face externa pintada com tinta acrílica, após o ensaio de estanqueidade à água, evidencia que a tinta acrílica foi capaz de selar as fissuras na superfície da argamassa e confirma que o tratamento da junta vertical com manta de elastômero EPDM apresentou bom desempenho quanto à estanqueidade à água.
In the context of steel constructions, it has been common the occurrence of watertightness problems in the joints and interfaces between masonry and steel structure, which leads to an early deterioration of the structure and decreases the service life of the building. This research aims to evaluate the performance in terms of watertightness of typical joints used in external vertical sealing systems (EVS) in masonry for steel structures, subjected to accelerated aging. For this purpose, a radiant panel was developed following the requirements of ABNT NBR 15575-4:2013 and two specimens of an experimental model with vertical joint were constructed. The joints of the experimental model were treated with a polyurethane sealant, and later treated with an EPDM rubber splice tape. It was carried out heat exposure and thermal shock tests and watertightness tests, based on the cited standard. In the case of joints treated with EPDM rubber splice tape, the watertightness tests were also carried out with the external face of the experimental model painted with acrylic paint. It was noted that after the heat exposure and thermal shock tests, the polyurethane sealant and the EPDM rubber splice tape did not suffer noticeable degradation and it was also noted that horizontal cracks appeared on the inner face of the specimens of the experimental model. The moisture spots identified on the experimental model during the water tightness tests occurred due to the passage of water through the horizontal cracks introduced in the heat exposure and thermal shock test and not by the vertical joint for both treatments. There are strong evidences that horizontal cracking may have been induced by the presence of the connectors inside the horizontal joints, which eventually transferred the displacement suffered by the steel pillar due to the expansion to the masonry. The absence of moisture spots on the experimental model with its external face painted with acrylic paint, after the watertightness test, shows that the acrylic paint was able to stagnate the cracks in the surface of the mortar and confirms that the treatment of the vertical joint with EPDM rubber splice tape showed good performance in terms of watertightness.
Palavras-chave: Aço - Estruturas
Vedação (Tecnologia)
Alvenaria
Juntas (Engenharia)
Desempenho
CNPq: Processos Construtivos
Editor: Universidade Federal de Viçosa
Titulação: Mestre em Engenharia Civil
Citação: FRANCO, Rayane Neves. Avaliação do desempenho quanto à estanqueidade de juntas sujeitas a envelhecimento acelerado, utilizadas em sistemas de vedação vertical externa em alvenaria para estruturas de aço. 2019. 153 f. Dissertação (Mestrado em Engenharia Civil) - Universidade Federal de Viçosa, Viçosa. 2019.
Tipo de Acesso: Acesso Aberto
URI: http://www.locus.ufv.br/handle/123456789/25076
Data do documento: 7-Fev-2019
Aparece nas coleções:Engenharia Civil

Arquivos associados a este item:
Arquivo Descrição TamanhoFormato 
texto completo.pdftexto completo8,22 MBAdobe PDFVisualizar/Abrir


Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.